RMRS FH32 shipbuilding steel plate

214 Views
10-May-2024

The RMRS FH32 shipbuilding steel plates have yield strength of 45,500 psi (315 MPa), and ultimate tensile strength of 64,000 - 85,000 psi (440-590 MPa). All the RMRS FH32 shipbuilding steel plate offered by KUNFENG Industry can be certificated by RMRS.

The application of RMRS FH32 shipbuilding steel plate

RMRS FH32 Shipbuilding steel plates can be used for producing container and bulk cargo vessels as well as cruise ships, ferries and yachts.

RMRS FH32 shipbuilding steel plate Chemical Composition

Grade	C %	Si %	Mn %	P %	S %	V %	AL %	Cr %
RMRS Grade FH32	0.160	0.1-0.5	0.90-1.6	0.025	0.025	0.05-0.10	0.015	0.200
	Cu %	Mo %	Nb %	Ni %	Ti %	N %
	0.350	0.080	0.02-0.05	0.800	0.020	0.009

RMRS FH32 shipbuilding steel plate Mechanical Properties

Grade	Thickness(mm)	MinYield(Mpa)	Tensile(Mpa)	Elongation (%)	Min Impact Energy
RMRS Grade FH32	8mm-50mm	Min 315Mpa	440-590Mpa	22%	-60	34J
	51mm-70mm	Min 315Mpa	440-590Mpa	22%	-60	41J
	71mm-100mm	Min 315Mpa	440-590Mpa	22%	-60	50J
The min impact energy is longitudinal energy

The rolling size of RMRS FH32 shipbuilding steel plate

Thickness	3-150mm
Width	1220-4200mm
Length	5000-18000mm

Notes: coil thickness ≤ 25mm
RMRS FH32 Shipbuilding steel plates are mainly used for making the hull of ship building and ship repairing, the offshore oil drilling platform, the platform pipe joints and other components. RMRS FH32 shipbuilding steel plate is a kind of hot rolled high tensile strength steel. RMRS FH32 shipbuilding steel plate can achieve the impact toughness at Celsius degree -60°. welcome to contact KUNFENG if you are looking for RMRS FH32 shipbuilding steel plate supplier.